PVC waterproof membranes
★Products Description
The PVC waterproofing rolls formulas are based upon polyvinyl chloride resin with other assistants added to provide flexibility and stability such as anti-oxidant,absorbent of ultraviolet light, plasticizer and plastic filling agent.
★Products Specification
Divided by the product composition: homogeneous non-composite membranes (code H), with fiber composite backing sheet (code L), fabric reinforced sheet (code P), glass fiber reinforced membrane within (code G), glass fibers increased with fiber composite backing sheet (code GL
Sheets of single-layer and laminated sheets with fibre felt or fibre as reinforced layers are supplied in our company.
Width : 1-2.0m
Thickness : 0.3- 2.0mm
Length: 15m- 100m
Products Hall
★GB12952-2003 Physical Properties
Item |
Specification |
|||||||
H |
L |
P |
G |
GL |
||||
The resin thickness of Middle fabric,mm≥ |
— |
0.40 |
||||||
Tensile Properties |
Maximum tension N/cm ≥ |
— |
120 |
250 |
— |
120 |
||
Tension strength Mpa≥ |
10 |
|
|
10 |
|
|||
Maximum tension elongation%≥ |
|
|
15 |
|
|
|||
Fracture elongation,%≥ |
200 |
150 |
|
200 |
100 |
|||
Heat treatment size change rate,%≤ |
2.0 |
1.0 |
0.5 |
0.1 |
0.1 |
|||
Low-temperature bending |
-25℃No crack |
|||||||
Water tightness |
0.3Mpa,2hNo seepage |
|||||||
Attack resistance |
0.5kg·m,No seepage |
|||||||
static charge resistance |
|
|
20kgNo seepage |
|||||
Seam strip strength,N/mm≥ |
4.0orMembranes break |
3.0 |
||||||
right-angle tear strength,N/mm≥ |
50 |
|
|
50 |
|
|||
Trapezoid tear strength,N≥ |
|
150 |
250 |
|
220 |
|||
Water absorption(70℃ 168h)% |
After soaking≤ |
4.0 |
||||||
air-cure later≥ |
-0.40 |
|||||||
Heat aging(80℃)
|
Time |
672h |
||||||
Appearance |
No blister,flaw,delamination,coherence,hole |
|||||||
Tensile strength retention,%≥ |
85 |
|||||||
Elongation rate of keeping,%≥ |
80 |
|||||||
Low temperature bend |
-20℃No crack |
|||||||
Chemistry resistance |
Appearance |
No blister,flaw,delamination,coherence,hole |
||||||
Tensile strength retention%≥ |
85 |
|||||||
Elongation rate of keeping%≥ |
80 |
|||||||
Low-temperature bending |
-20℃No crack |
|||||||
Artificial weather accelerated aging |
Time |
1500hb |
||||||
Appearance |
No blister,flaw,delamination,coherence,hole |
|||||||
Tensile strength retention%≥ |
85 |
|||||||
Elongation rate of keeping%≥ |
80 |
|||||||
Low temperature bend |
-20℃No crack |
★Application Range
PVC membranes form an effective barrier to liquid water or water vapor in the roof construction for industrial and civil engineering, underground engineering such as subway & tunnel, water conservancy such as water pools & ditch, shelterindustrial plants, steel plants, grain depot, land filling, dyke, sewage treatment and basement.
Copyright Qingdao shendun Waterproof Technology Co. Ltd. E-mail:sdfs@cnshendun.com
ADD:No.32 Siyuan Road High Tech Industrial Development Zone Qingdao
Domestic:+86-532-66723991 +86-532-66783992 +86-532-66723993 +86-532-66723995 +86-13963929278
Copyright Qingdao shendun Waterproof Technology Co. Ltd.
E-mail:sdfs@cnshendun.com
ADD:No.32 Siyuan Road High Tech Industrial Development Zone Qingdao
Domestic:+86-532-66723991