TPO Root-resistant Puncture Waterproof Membrane

Category: Polymer waterproofing membrane system

key word: Polymer waterproofing membrane system

Contact Phone:

+86-532-66723991

Inquiry Return to List

Product Details

★Product Description

Thermoplastic polyolefin (TPO) waterproofing membrane is a kind of ethylene resin as the base material, the use of advanced polymerization technology and a specific formula made of sheet thermoplastic rubber elastic waterproof material, is popular in the United States and Europe in recent years, a new material, the ingredients do not contain plasticizer, there is no plasticizer migration and brittle. It has the comprehensive characteristics of high tensile strength, good wear resistance, strong UV resistance, smooth surface, high reflectivity and pollution resistance. Easy to process, can be welded, convenient construction, completely recycled, green new waterproof material.

☆Features:

Using advanced polymerization technology and special formula, without any plasticizer, to maintain long-term weather resistance;

With high tear strength, breaking strength and puncture resistance;

Through thermal welding can form stronger than the coil seam, welding seam surface is smooth, continuous and uniform;

The gray and black bottom reinforced coil has high reflectivity. The coil does not contain chlorinated polymer and chlorine gas, which is conducive to environmental protection and construction safety.

★Product types and specifications

According to the classification of products, it is divided into: homogeneous non-composite coil (code H), composite coil with fiber backing (code L), and reinforced coil in fabric (code P)

Length: ≥ 20 m Width: 2.0 m

Thickness: 0.5mm 1.0mm 1.2mm 1.5mm 2.0mm

Color: black, white, green, etc., can be customized according to customer requirements (two-color coil can also be customized).

Test Item			Indicators
			H		L			P
Thickness of resin layer above intermediate fabric, mm≥			—					0.40
Maximum pulling force, N/cm ≥			—		200			250
Tensile strength, MPa ≥			12
Elongation at maximum tension,%≥								15
Elongation at break,%≥			500		250
Dimensional change rate of heat treatment,%≤			2.0		1.0			0.5
Low temperature bending			No crack at -40 ℃
impervious to water			0.3Mpa,2h impervious
Impact resistance			0.5kg · m, impervious to water
anti-static load^a			—			20kg impervious
Joint peel strength, N/mm ≥			4.0 or coil damage			3.0
Right-angle tear strength, N/mm≥			60				60
Trapezoidal tear strength, N≥			—	300		450			350
water absorption (168h at 70 ℃),%		After immersion ≤	4.0
		After drying ≥	-0.40
thermal aging (115 ℃)	Time		672h
	Appearance		No blisters, cracks, delaminations, bonds and holes
	Retention rate of tensile strength (maximum tensile force),%≥		90
	Elongation retention rate,%≥		90
	Low temperature bending		No crack at -40 ℃
Chemical resistance	Appearance		No blisters, cracks, delaminations, bonds and holes
	Retention rate of tensile strength (maximum tensile force),%≥		90
	Elongation retention rate,%≥		90
	Low temperature bending		No crack at -40 ℃
Artificial climate accelerated aging	Time		1500h^b
	Appearance		No blisters, cracks, delaminations, bonds and holes
	Retention rate of tensile strength (maximum tensile force),%≥		90
	Elongation retention rate,%≥		90
	Low temperature bending		No crack at -40 ℃
a Static load resistance is only applied to roll material of pressed roof. B the artificial climate accelerated aging time of the products used in single-layer coiled material roofing is 2500h.

★Scope of application

It can be widely used in permanent waterproof engineering of roofs, basements, subways, dams, water conservancy, tunnels and steel structure roofs, large supermarkets and large factories